贾燕1,赵永涛2,张红松2

为确定ZrO2/莫来石热障涂层的单层最佳厚度,采用有限元技术研究单层厚度对ZrO2/莫来石热障涂层热冲击应力的影响。结果表明,莫来石层厚度为0.25mm时,涂层表面及ZrO2/莫来石界面处具有最大热应力,而其它莫来石层厚度时涂层内部热应力则受莫来石层厚度影响不明显。当ZrO2层厚度为0.3mm时,ZrO2/莫来石涂层中的热应力在整个横向距离范围内保持稳定,而其它情况下涂层中的热应力则与ZrO2层厚度成正比。涂层表面处的径向热应力大于ZrO2/莫来石界面处的对应值。     

High-temperature behavior of oxide dispersion strengthening CoNiCrAlY

To fabricate oxide dispersion strengthened bond coatings, commercial Co–30wt-%Ni–20Cr–8Al–0?4Y powder was milled with 2% additions of Al₂O₃, Y₂O₃ or Y₂O₃ + HfO₂. Low-pressure plasma sprayed, free-standing specimens were oxidised in air + 10%H2O at 1100 °C both isothermally (100 h) and in 500, 1?h cycles. Dry air cyclic testing conducted at both ORNL and FZJ showed remarkably similar results. In general, the water vapour addition caused more scale spallation. Two LPPS specimens without oxide additions were tested for comparison. The specimens with 2%Al₂O₃ addition exhibited the best behaviour as the powder already contained 0?4%Y. Additions of 2%Y₂O₃ and especially 1%Y₂O₃ + 1%HfO₂ resulted in over-doping as evidenced by high mass gains and the formation of Y- and Hf-rich pegs. Scanning transmission electron microscopy of the isothermal specimens showed no Hf and/or Y segregation to the alumina scale grain boundaries in the over-doped specimens.     

Dual-phase rare-earth-zirconate high-entropy ceramics with glass-like thermal conductivity

A series of rare earth zirconates (RE₂Zr₂O₇) high-entropy ceramics with single- and dual-phase structure were prepared. Compared with La₂Zr₂O₇ and Yb₂Zr₂O₇, the smaller “rattling” ions (Yb³⁺, Er³⁺, Y³⁺) have been incorporated into pyrochlore lattice in (La_0.2Nd_0.2Y_0.2Er_0.2Yb_0.2)₂Zr₂O₇ (LNYEY) while larger ions (La³⁺, Nd³⁺, Sm³⁺, Eu³⁺) incorporated into fluorite lattice in (La_0.2Nd_0.2Sm_0.2Gd_0.2Yb_0.2)₂Zr₂O₇ (LNSGY). Due to high-entropy lattice distortion and resonant scattering derived from smaller ions Yb³⁺, Er³⁺, and Y³⁺, LNYEY shows a lower glass-like thermal conductivity (1.62-1.59 W m^-1 K^-1, 100-600℃) than LNSGY (1.74-1.75 W m^-1 K^-1, 100-600℃). Moreover, LNYEY and LNSGY exhibit enhanced Vickers’ hardness (LNYEY, H_v = 11.47 ± 0.41 GPa; LNSGY, H_v = 10.96 ± 0.26 GPa) and thermal expansion coefficients (LNYEY, 10.45 × 10^-6 K^-1, 1000℃; LNSGY, 11.02 × 10^-6 K^-1, 1000℃). These results indicate that dual-phase rare-earth-zirconate high-entropy ceramics could be desirable for thermal barrier coatings.     

Microstructure,tribological behavior and magnetic properties of Fe−Ni−TiO2 composite coatings synthesized via pulse frequency variation

The Fe−Ni−TiO₂ nanocomposite coatings were electrodeposited by pulse frequency variation. The results showed that the nanocomposite with a very dense coating surface and a nanocrystalline structure was produced at higher frequencies. By increasing the pulse frequency from 10 to 500 Hz, the iron and TiO₂ nanoparticles contentswere increased in expense of nickel content. XRD patterns showed that by increasing the frequency to 500 Hz, an enhancement ofBCC phase was observed and the grain size of deposits was reduced to 35 nm. The microhardness and the surface roughness were increased to 647 HV and 125 nm at 500 Hz due to the grain size reduction and higher incorporation of TiO₂ nanoparticles into the Fe−Ni matrix (5.13 wt.%). Moreover, the friction coefficient and wear rate values were decreased by increasing the pulse frequency;while the saturation magnetization and coercivity values of the composite deposits were increased.     

Effect of heat treatment and zircon addition on the properties of low-cement castables based on recycled alumina grog

In this investigation, low-cement castables were prepared using 70% alumina grog aggregates obtained from crushed alumina brick waste. The aggregates were thermally treated at 1550 °C for 3 h. Four types of low-cement castables were prepared with various types of aggregates (alumina grog with or without thermal treatment) and fillers (with or without zircon addition), and they were evaluated in terms of their physical, thermal, and chemical properties. Microstructural analysis via scanning electron microscopy (SEM) was performed on the castables before and after slag attack. Compared to the other fabricated castables, the thermally treated alumina grog castables with zircon showed better physical properties, such as a higher bulk density, cold crushing strength, and modulus of rupture and a lower apparent porosity and water absorption. In addition, they had a higher positive linear thermal expansion, refractoriness under load, permanent linear change, and hot modulus of rupture. The results of the SEM with energy dispersive X-ray analysis of the prepared castables confirmed that the mullite and anorthite phases were predominant when zircon was not added and the zircon–mullite phase additionally appeared upon the incorporation of zircon. A quantitative elemental analysis via X-ray fluorescence spectroscopy was employed to determine the composition of the castables. X-ray diffraction analysis showed that the alumina grog castables had a high mullite and low anorthite content, and the thermally treated alumina grog had a high anorthite, low mullite, and high zircon content. The improvement in the mechanical and thermo-mechanical properties of the castables with thermally treated alumina grog and added zircon can be attributed to the formation of the zircon–mullite phase with a low mullite phase content.     

New water-soluble copolymers of 2-methacryloyloxyethyl phosphorylcholine for surface modification

New copolymers of 2-methacryloyloxyethyl phosphorylcholine with 2-Deoxy-2-methacrylamido-D-glucose, N-vinylpyrrolidone, and N-vinyl-N-methylacetamide were synthesized and characterized; the obtained copolymers contained 10–50 mol% of phosphorylcholine moieties, and their molecular masses ranged from 1.05 × 10⁵ to 4.40 × 10⁵. Reactivity ratios of the monomers were estimated. Conformational states of the copolymers in aqueous solutions were studied. The synthesized copolymer was grafted onto the surface of carbon fiber biosorbent using γ-radiation.     

Multivariate process trajectories for molecular description of MF thermal curing and correlation with hydrolytic stability

During curing of thermosetting resins the technologically relevant properties of binders and coatings develop. However, curing is difficult to monitor due to the multitude of chemical and physical processes taking place. Precise prediction of specific technological properties based on molecular properties is very difficult. In this study, the potential of principal component analysis (PCA) and principal component regression (PCR) in the analysis of Fourier transform infrared (FTIR) spectra is demonstrated using the example of melamine-formaldehyde (MF) resin curing in solid state. FTIR/PCA-based reaction trajectories are used to visualize the influence of temperature on isothermal cure. An FTIR/PCR model for predicting the hydrolysis resistance of cured MF resin from their spectral fingerprints is presented which illustrates the advantages of FTIR/PCR compared to the combination differential scanning calorimetry/isoconversional kinetic analysis. The presented methodology is transferable to the curing reactions of any thermosetting resin and can be applied to model other technologically relevant final properties as well.     

Influence of aluminum phosphate on the tribocorrosion performance of chemically bonded phosphate ceramic coatings

In this study, chemically bonded phosphate ceramic coatings (CBPCCs) with different contents of aluminum phosphate (AP) are prepared on stainless steel (AISI 304L). Differential scanning calorimetry, X-ray diffraction, contact angle test, and a tribocorrosion experiment are carried out to clarify the role of AP in the tribocorrosion performance of CBPCCs. The results show that, with the increase in the AP content, the enthalpy of curing increases because of the greater formation of the bonding phase AlPO₄. Both in static corrosion and in tribocorrosion, the corrosion current density of CBPCCs achieves the lowest value when the weight ratio of AP to polytetrafluoroethylene is about 0.78. Additionally, the influence mechanism of AP on tribocorrosion is clarified. AlPO₄ from the reaction between AP and Al₂O₃ has excellent mechanical properties and can enhance the wear resistance of CBPCCs by reducing the mechanical wear and the increased wear due to corrosion. The alumina particles wrapped by AlPO₄ can form a dense and smooth surface and change the direction of electrolyte propagation, which leads to the increase in the tribocorrosion resistance of CBPCCs.